2014

(12) PATENT APPLICATION PUBLICATION (19) INDIA (22) Date of filing of Application :31/12/2014

(21) Application No. : 1369/KOL/2014 (43) Publication Date : 22/07/2016         Journal No. ­ 30/2016

  (54) Title of the invention : PRODUCT AND PROCESS FOR MANUFACTURING SUPERIOR QUALITY COMPLEX MICROSTRUCTUREREINFORCEMENT REBARS FOR EARTHQUAKE RESISTANCE APPLICATIONS   (51) International classification :E04B2/56 (31) Priority Document No :NA (32) Priority Date :NA (33) Name of priority country :NA (86) International Application No :NA         Filing Date :NA (87) International Publication No : NA (61) Patent of Addition to Application Number :NA         Filing Date :NA (62) Divisional to Application Number :NA         Filing Date :NA

  (71)Name of Applicant :     1)Tata Steel Limited       Address of Applicant :Jamshedpur­831001, India Jharkhand India (72)Name of Inventor :    1)Shaumik Lenka (India)    2)Jayanta Chakraborty (India)    3)Diptak Bhattacharya (India)    4)Saurabh Kundu (India)    5)Kandala S Ramakrishna (India)    6)Ravinder Singh Pathania (India)    7)Sanjay Chandra (India)    8)T.Venugopalan (India)

(57) Abstract : A process for manufacturing steel rebar is described having steps of casting billet / bloom with chemical composition of 0.05 ­ 0.3 wt.% carbon, 0.4 ­ 1.65 wt.% manganese, 0.1 ­ 0.8 wt.% silicon, up to 0.05 wt.% niobium, up to 0.05 wt.% vanadium, up to 0.05 wt.% titanium, up to 0.05 wt.% aluminum, up to 0.04 wt.% Sulphur and phosphorous, up to 0.012 wt.% of nitrogen and 0.0005 to 0.01 wt.% boron and the balance being iron and impurities, and thermo­mechanical rolling of the billet / bloom into rebar with FRT of 980­1100 deg. C and equalization temperature of 600­680 deg. C for 6­12mm diameter and 540­640 deg. C for 16 ­ 40 mm diameter.   Number of Pages = 21 Best View in Resolution of 1024x768 or later. Enable Javascript for Better Performance.