Resistance to deformation under compression (DIN 53576/B). Crushing ... In
alkaline solution (NaC1 25%) DIN. 53428. 0.26. 137. +1. In water DIN 53428.
0.27.
dd
CF15
PVC Foam
Grade: Colour: Density: Width: Thickness (mm): Roll Length:
CBF812 White/Brown/Grey/Black 120kgs/m3 1000mm – 1400mm 2,3,4,5,6,8,10,12,15,18,20 25 – 100 meters according to the thickness
Description Resistance to deformation under compression (DIN 53576/B) Crushing on initial thickness of 25% Crushing on initial thickness of 40% Crushing on initial thickness of 65%
Result N 69.7 109.7 301.0
Resistance to deformation under compression (DIN 53572) Room temperature, crushing 50%, 72 hours Residual deformation after 30 hours Residual deformation after 4 hours Residual deformation after 24 hours
Resistance to tensile strength/maximum extension (DIN 53571), and change in terms of dimensions of original sample and after different treatments/ageing. DESCRIPTION Original Sample Warm (60°C) Cold (-30°C) Ageing 24hrs in steam (hydrolysis 100°C DIN 53578) In mineral oil DIN 53428 In alcohol DIN 53428 In alkaline solution (NaC1 25%) DIN 53428 In water DIN 53428 In petrol (iso-octane) DIN 53428 In concentrated acid solution (H2SO4 40%) DIN 53428 In concentrated alkaline solution (NaOH 40%) DIN 53428
TRACT (n/mm2) 0.24 0.23 0.28
EXTENS. (%) 137 177 131
-1 -0.6
0.24
157
+1
0.48 0.40
66 25
+1 -11
0.26
137
+1
0.27 0.57
133 38
+2 -7
0.26
137
+1
0.27
135
+3
AVGE. DIM. VA (%)
The above figures are average values. We recommend evaluation prior to use to ascertain the suitability of the material for the application.