Abstract. A hybrid technique for the selective growth of ZnO nanorod arrays on wanted areas of thin cover glass substrates was developed without the use of ...
Nanoscale Res Lett (2010) 5:669–674 DOI 10.1007/s11671-009-9504-6

NANO PERSPECTIVES

Seedless Pattern Growth of Quasi-Aligned ZnO Nanorod Arrays on Cover Glass Substrates in Solution Q. Ahsanulhaq • Jin Hwan Kim • Jeong Hyun Kim Y. B. Hahn



Received: 28 August 2009 / Accepted: 1 December 2009 / Published online: 27 December 2009 Ó The Author(s) 2009. This article is published with open access at Springerlink.com

Abstract A hybrid technique for the selective growth of ZnO nanorod arrays on wanted areas of thin cover glass substrates was developed without the use of seed layer of ZnO. This method utilizes electron-beam lithography for pattern transfer on seedless substrate, followed by solution method for the bottom-up growth of ZnO nanorod arrays on the patterned substrates. The arrays of highly crystalline ZnO nanorods having diameter of 60 ± 10 nm and length of 750 ± 50 nm were selectively grown on different shape patterns and exhibited a remarkable uniformity in terms of diameter, length, and density. The room temperature cathodluminescence measurements showed a strong ultraviolet emission at 381 nm and broad visible emission at 585–610 nm were observed in the spectrum. Keywords ZnO nanorod arrays  Seedless pattern growth  Hybrid method

Introduction One-dimensional (1D) ZnO nanostructure arrays aligned on substrates are highly desirable for promising device applications. For example, it has been demonstrated that ZnO nanorod/nanowire arrays on proper substrates can emit ultraviolet

Q. Ahsanulhaq  J. H. Kim  J. H. Kim  Y. B. Hahn (&) School of Semiconductor and Chemical Engineering, Department of BIN Technology, and Nanomaterials Processing Research Centre, Chonbuk National University, Jeonju 561-756, South Korea e-mail: [email protected] Q. Ahsanulhaq Faculty of Engineering, Toyama University, 3190 Gofuku, Toyama 930-8555, Japan

laser at room temperature [1], enhance biofluorescence detection [2], act as piezoelectric nanogenerators [3], and can be used to construct nanowire dye-sensitized solar cells [4]. Moreover, ZnO nanorod arrays (NRAs) are expected to find potential applications as nano-optoelectronic devices [5–11]. For the growth of aligned and quasi-aligned ZnO NRAs on substrates, various low temperature solution-phase approaches have recently been developed because of their good potential for scale-up production and commercial feasibility. A selective area growth of well-aligned ZnO nanostructures has also been achieved using various techniques like templatedirected approach [12], nanosphere lithography [13], polystyrene microsphere-based self-assembly monolayers [14], silane-based self-assembled monolayers [15], and conventional photolithography [16]. However, these patterning methods require expensive mask, complex multi-step processes, and metal catalysts in some cases, and deposition of seed layer on substrates. In general, it is known that the seed layer of ZnO is required for the growth of ZnO nanorods without the use of catalyst. The ability to control the nanorod orientation and position during the growth is critically important, because it allows the growth and assembly of nanorods to be combined into one step, facilitates the subsequent fabrication processes such as the formation of electrical contacts to nanorods and opens up the design space for novel devices. Achieving spatially, specific, selective, highly ordered, and uniform growth of ZnO NRAs on wanted areas of substrates via a one-step approach by solution method without using seed layer remains a prominent challenge, although impressive progresses have been made using seeded substrates [17, 18]. In this paper, we report the growth of quasi-aligned ZnO NRAs on a thin cover glass substrate in solution without the use of any seed layer. The position and location of

123

670

NRAs was controlled by electron-beam lithography patterns. The ZnO NRAs were grown on the patterned cover glass substrate in solution at 90 °C. We chose cover glass substrate to grow NRAs because it possesses many attractive properties including biocompatibility, lightweight, and transparency. Particularly, the ZnO NRAs on cover glass open a wide variety of application; examples are enhancement of fluorescence detection, single native DNA molecule detection and can act as novel carriers for mammalian cell transfection [2, 19].

Experimental The nanofabrication process used in this work was accomplished in four steps as shown in Fig. 1: (a) thin layer of resist polymer spun over cover glass substrate; (b) electron-beam writing; (c) growth of ZnO nanorods arrays in solution; and (d) lift-off resist material and residue from the substrate. Polymethylmethacrylate (PMMA) was used as electronbeam resist material and spin-coated over the substrate. After writing, the patterned substrates were developed in a solution of methyl isobutyl ketone and isopropyl alcohol (volume ratio of 1:3) for 30 s. For the growth of ZnO nanostructures Fig. 1 Schematic illustration of selective growth process of ZnO nanorod arrays: a thin layer of resist polymer (PMMA) spun over cover glass substrate; b pattern transfer by electronbeam lithography; c growth of aligned ZnO nanorod arrays in solution, and d lift-off resist material and residue from the substrate

123

Nanoscale Res Lett (2010) 5:669–674

on the patterned substrates, 10 mM aqueous solution of zinc nitrate hexahydrate (Zn(NO3)26H2O, Sigma–Aldrich) and water-soluble hexamethylenetetramine (C6H12N4, Sigma– Aldrich) were used as reagents. In a typical reaction, the pH of solution was kept at 6 * 7. The pre-patterned cover glass substrates were immersed in the solution, and the temperature of flask was kept constant at 90 °C for 6 h. After the successful growth of nanorods, the electron-beam resist material was lifted off from the substrate using organic solvents. The surface morphologies of as-grown ZnO nanorod arrays were examined by field emission scanning electron microscopy (FESEM), (FESEM, Hitachi, Japan). An X-ray diffractometer (XRD) (Rigaku III/A, Japan) was used to analyze crystal phase and crystallinity of ZnO NRAs. X-ray wavelength used in the analysis was 0.154 nm of Cu Ka. The room temperature cathodluminescence (CL) spectra and images were taken using CL system equipped on a high resolution FESEM (FESEM, Hitachi, Japan).

Results and Discussion Figure 2 shows the FESEM images of ZnO NRAs, selectively grown on cover glass substrates. The interdistance

Nanoscale Res Lett (2010) 5:669–674

between two strips is kept 3 lm, and each strip has length of 20 lm (a). The magnified image of (a) clearly identifies high degree site-selective growth of NRAs (b). The gap between the two strips and length of patterns was same; however, the patterned site further reduced to 1.5 lm and shown in (c). As can be seen in the magnified FESEM images of ZnO NRAs (b and d), the patterned sites are fully occupied with ZnO nanorods. The ability to scale up the pattern to a larger size has also been examined. Figure 2e shows the low-magnification FESEM image of large size square-shape pattern (100 9 100 lm), where each white spot represents the patterned ZnO NRAs. The inset image of Fig. 2e shows ZnO nanorods on a thin cover glass substrate. The magnified image (f) represents that each nanorod exhibits hexagonal nanotip. The inset in (f) represents a magnified square pattern of 4 lm 9 4 lm. It can be seen that high-density NRAs were grown only on both microstrip and microsquare patterns, while no NRAs were grown in the interstrip and intersquare areas. Each nanorod has a diameter of 60 – 10 nm and length of 550 – 50 nm, respectively. More interestingly, these quasi-aligned ZnO

671

NRAs on different shape patterns exhibit remarkable uniformity in terms of diameter, length, and density since they are grown under same experimental conditions. Figure 3a shows the XRD pattern of the ZnO NRAs selectively grown on pre-patterned cover glass substrates. A sharp, strong, and dominant peak of ZnO (0002) at 34.24° observed, indicating that the synthesized nanorod arrays are single crystalline in nature and grown along the c-axis direction. Moreover, the strong intensity of (0002) reflection with narrow width also exhibits that the ZnO NRAs are well oriented along the normal direction of the substrate surface, which is almost consistent with the FESEM observations. TEM image of a ZnO nanorod is presented in Fig. 3b, and SAED pattern of ZnO nanorod is represented as Fig. 3c. These results confirmed that the ZnO NRAs were single crystal in nature. ZnO nanorods were formed by the hydrolysis of zinc nitrate hexahydrate in water in the presence of hexamethylenetetramine (HMTA). HMTA is a nonionic cyclic tertiary amine that can act as a Lewis base with metal ions and a bidentate ligand capable of bridging two zinc(II) ions in

Fig. 2 FESEM images of ZnO nanorod arrays: a low- and b high-magnification images of ZnO NRAs grown on 2-lm strip patterns; c low- and d highmagnification images of ZnO NRAs grown on 500-nm strip patterns; e low- and f highmagnification images of ZnO NRAs grown on square patterns

123

672

Nanoscale Res Lett (2010) 5:669–674

Fig. 3 a XRD pattern of ZnO nanorod arrays grown on glass substrate; b TEM image of single ZnO nanorod and c its corresponding SAED pattern

solution [20]. HMTA can also hydrolyze to generate formaldehyde and ammonia under the known reaction conditions [21]. It is considered that HMTA slowly decomposes and afford steady supply of ammonia, which can form ammonium hydroxide and complex with zinc (II) to form Zn(NH3)2? 4 [22, 23]. Zinc (II) is thought to exist mainly as Zn(OH)24 and Zn(NH3)2? 4 under the given pH and temperature. Consequently, the formation of ZnO occurs by dehydration of these reaction intermediates [24]. The comprehensive chemical reaction represented below. C6 H12 N4 þ 6H2 O $ 6CH2 O þ 4NH3

ð1Þ

C6 H12 N4 þ Zn2þ ! ½ZnðC6 H12 N4 Þ2þ

ð2Þ

 NH3 þ H2 O ! NHþ 4 þ OH

ð3Þ

Zn(NH3 Þ2þ 4

ð4Þ

Zn(OH)2 4

ð5Þ

Zn2þ þ 4NH3 ! Zn





þ 4OH !

 Zn(NH3 Þ2þ 4 þ 2OH ! ZnO þ 4NH3 þ H2 O

ð6Þ

 Zn(OH)2 4 ! ZnO þ H2 O þ 2OH

ð7Þ

the cover glass substrate. This causes elevated concentration of ZnO precursors to become confined to a small area on patterned sites of the cover glass substrate. In this way, enhanced nucleation can be obtained on the seedless patterned cover glass substrates. The orientation of crystal is highly uniform with in each patterned site, implying that atomic level interfacial structure may also control the nucleating plane of crystals. This method demonstrates that it is possible to obtain highly specific growth of crystals in a constrained crystallographic direction by combining patterning process with bottom-up solution approach. The patterned spot helps the nucleated ZnO to grow in quasialigned direction on the electron-beam exposed sites. Controlling the size of microstrip and microsquare-shape patterns simultaneously controls the density and quasialignment of NRAs. Thus, by adjusting the concentration of zinc nitrate, temperature, reaction time, and substrate patterning we could control the most important characteristics of anisotropic crystallization process: that is, location, density, and anisotropic crystallographic orientation. In this way, we can grow nanorod arrays on patterned substrates with different desirable configurations. The microscopic spectral-emission characteristic of ZnO NRAs was directly imaged by highly spectrally and spatially resolved scanning CL microscopy. Since the CL microscopy has the advantage of a much higher lateral and depth resolution when compared to photoluminescence, it is a unique tool for the investigation of nanometer-scaled structures. Figure 4c shows room temperature CL spectrum of periodically grown ZnO NRAs on cover glass substrates. A strong ultraviolet (UV) emission at 381 nm and a broad visible emission at 585–610 nm were observed in the spectrum. The UV emission is the band-edge emission resulting from the recombination of excitonic centers [25]. The visible luminescence band appears broad, composed of yellow-orange and red part of the spectrum and is known to be attributed to native defects, oxygen interstitial defects and/or nonradiative recombination centers. Figure 4b and c show the low-magnification FESEM image of ZnO NRAs grown on square pattern, showing clearly well-defined squares of ZnO NRAs, and the corresponding monochromatic CL images taken from the samples, respectively. The CL images were taken under the same microscope and monochromator conditions. Bright areas in Fig. 4c revealed the luminescence sites, which coincide with the location and position of patterned NRAs.

½Zn(C6 H12 N4 Þ2þ þ 2OH ! ZnO þ H2 O þ C6 H12 N4 ð8Þ We assume that the reaction pH and temperature facilitates the positively charged [Zn(C6H12N4)]2? and Zn(NH3)2? 4 intermediates to migrate on patterned spots on

123

Summary and Conclusion In summary, the ZnO nanorod arrays were successfully grown on patterned glass substrates without the use of seed

Nanoscale Res Lett (2010) 5:669–674

673

room temperature CL measurements showed a strong ultraviolet (UV) emission at 381 nm and a broad visible emission at 585–610 nm. The developed hybrid method is a simple, environmentally friendly system for the direct production, deposition, and patterning of nanostructures on a seedless surface. This seedless procedure could replace the multitude of competing complex processes presently in use. Moreover, this approach is generic and could easily be modified for any desired metal oxide with very few limitations. Acknowledgment This work was supported by the Korean government (MEST) through the Pioneer Research Center for Artificial Mechanosensory System (grant number 2009-0082837). Open Access This article is distributed under the terms of the Creative Commons Attribution Noncommercial License which permits any noncommercial use, distribution, and reproduction in any medium, provided the original author(s) and source are credited.

References

Fig. 4 a CL spectrum of ZnO nanowires arrays grown over square patterns. b FESEM image of ZnO NRAs grown on square pattern and c luminescence image taken from b

layer of ZnO by solution method at 90 °C. Electron-beam lithography process controlled the alignment, position, and location of NRAs. The arrays of highly crystalline ZnO nanorods having diameter of 60 – 10 nm and length of 750 – 50 nm were selectively grown on glass substrates, which have different shapes of patterns and exhibited a remarkable uniformity in terms of diameter, length, and density. XRD spectrum showed a strong and dominant peak of ZnO (0002), grown along c-axis direction. The

1. M.H. Huang, S. Mao, H. Feick, H. Yan, Y. Wu, H. Kind, E. Weber, R. Russo, P. Yang, Science 292, 1897 (2001) 2. A. Dorfman, N. Kumar, J. Hahm, Langmuir 22, 4890 (2006) 3. Z.L. Wang, J. Song, Science 312, 242 (2006) 4. P. Ravirajan, A.M. Peiro, M.K. Nazeeruddin, M. Graetzel, D.D.C. Bradley, J.R. Durrant, J. Nelson, J. Phys. Chem. B 110, 7635 (2006) 5. N.K. Reddy, Q. Ahsanulhaq, J.H. Kim, M. Devika, Y.B. Hahn, Nanotechnology 18, 445710 (2007) 6. N.K. Reddy, Q. Ahsanulhaq, J.H. Kim, Y.B. Hahn, Appl. Phys. Lett. 92, 043127 (2008) 7. N.K. Reddy, Q. Ahsanulhaq, J.H. Kim, Y.B. Hahn, Europhys. Lett. 81, 38001 (2008) 8. N.K. Reddy, Q. Ahsanulhaq, Y.B. Hahn, App. Phys. Lett. 93, 083124 (2008) 9. C. Yan, J. Liu, F. Liu, J. Wu, K. Gao, D. Xue, Nanoscale Res. Lett. 3, 473 (2008) 10. C. Yan, D. Xue, J. Phys. Chem. B 110, 25850 (2006) 11. C. Yan, D. Xue, Electrochem. Commun. 9, 1247 (2007) 12. J.H. Fan, W. Lee, R. Hauschild, M. Alexe, G.L. Rhun, R. Scholz, A. Dadgar, K. Nielsch, H. Kalt, A. Krost, M. Zacharias, U. Gcsele, Small 2, 561 (2006) 13. J.H. Fan, B. Fuhrmann, R. Scholz, F. Syrowatka, A. Dadgar, A. Krost, M. Zacharias, J. Crystal Growth 287, 34 (2006) 14. D.F. Liu, Y.J. Xiang, C.X. Wu, X.Z. Zhang, L.F. Liu, L. Song, W.X. Zhao, D.S. Luo, J.W. Ma, J. Shen, Y.W. Zhou, G. Wang, Y.C. Wang, S.S. Xie, Nano Lett. 10, 2375 (2006) 15. Y. Masuda, N. Kinoshita, F. Sato, K. Koumoto, Cryst. Growth Des. 6, 75 (2006) 16. Y. Tak, K. Yong, J. Phys. Chem. B 109, 19263 (2005) 17. Q. Ahsanulhaq, J.H. Kim, Y.B. Hahn, Nanotechnology 18, 485307 (2007) 18. Q. Ahsanulhaq, A. Umar, Y.B. Hahn, Nanotechnology 18, 115603 (2007) 19. L. Nie, L. Gao, X. Yan, T. Wang, Nanotechnology 18, 015101 (2007) 20. L.E. Greene, B.D. Yuhas, M. Law, D. Zitoun, P. Yang, Inorg. Chem. 45, 7535 (2006)

123

674 21. G.J. Strom, W.H. Jun, J. Pharm. Sci. 69, 1261 (1980) 22. K. Govender, S.D. Boyle, B.P. Kenway, P. O’Brien, J. Mater. Chem. 14, 2575 (2004) 23. Z. Wang, X.F. Qian, J. Yin, K.Z. Zhu, Langmuir 20, 3441 (2004)

123

Nanoscale Res Lett (2010) 5:669–674 24. Q. Li, V. Kumar, Y. Li, H. Zhang, T.J. Marks, R.P.H. Chang, Chem. Mater. 17, 1001 (2005) 25. V. Srikant, D.R. Clarke, J. Appl. Phys. 83, 5447 (1998)