Feb 15, 2018 - Hiromi Yuasa 1, 2,a) , Fumiya Nakata1, Ryohei Nakamura1, and Yuichiro ..... 1 K. Uchida, S. Takahashi, K. Harii, J. Ieda, W. Koshibae, K. Ando, ...
Journal of Physics D: Applied Physics
ACCEPTED MANUSCRIPT • OPEN ACCESS
Spin Seebeck coefficient enhancement by using Ta50W50 alloy and YIG/Ru interface To cite this article before publication: Hiromi Yuasa et al 2018 J. Phys. D: Appl. Phys. in press https://doi.org/10.1088/1361-6463/aaaf89
Manuscript version: Accepted Manuscript Accepted Manuscript is “the version of the article accepted for publication including all changes made as a result of the peer review process, and which may also include the addition to the article by IOP Publishing of a header, an article ID, a cover sheet and/or an ‘Accepted Manuscript’ watermark, but excluding any other editing, typesetting or other changes made by IOP Publishing and/or its licensors” This Accepted Manuscript is © 2018 IOP Publishing Ltd.
As the Version of Record of this article is going to be / has been published on a gold open access basis under a CC BY 3.0 licence, this Accepted Manuscript is available for reuse under a CC BY 3.0 licence immediately. Everyone is permitted to use all or part of the original content in this article, provided that they adhere to all the terms of the licence https://creativecommons.org/licences/by/3.0 Although reasonable endeavours have been taken to obtain all necessary permissions from third parties to include their copyrighted content within this article, their full citation and copyright line may not be present in this Accepted Manuscript version. Before using any content from this article, please refer to the Version of Record on IOPscience once published for full citation and copyright details, as permissions may be required. All third party content is fully copyright protected and is not published on a gold open access basis under a CC BY licence, unless that is specifically stated in the figure caption in the Version of Record. View the article online for updates and enhancements.
This content was downloaded from IP address 51.255.83.114 on 15/02/2018 at 17:07
Page 1 of 15
us cri
YIG/Ru interface
pt
Spin Seebeck coefficient enhancement using Ta50W50 alloy and
Hiromi Yuasa 1, 2,a) , Fumiya Nakata1, Ryohei Nakamura1, and Yuichiro Kurokawa1 1
Graduate School of Information Science and Electrical Engineering, Kyushu University, Fukuoka 819-0395, Japan
PRESTO, Japan Science and Technology Agency, Kawaguchi, 332-0012, Japan
an
2
Abstract
This paper reports that Ta50W50 alloy has a higher spin Hall angle than that of -W by
dM
measuring the spin Seebeck coefficients for Fe5Y3O12 (YIG)/Ru/Ta50W50 and YIG/Ru/W systems. The spin Seebeck coefficient increased by inserting Ru, and the YIG/Ru/Ta50W50 system achieved 2.4 times the magnitude of spin Seebeck coefficient of the conventional YIG/Pt system although Ru and Ta50W50 have spin Hall angles with opposite signs. Ru seems to recover the spin mixing conductance that is decreased by Ta–W oxidation at its interface
pte
with YIG. To enhance the spin Seebeck coefficient, materials having a high spin Hall angle
ce
can be combined with materials having a high spin mixing conductance.
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
1
1.
Introduction
The spin Seebeck effect in a magnetic material is the spin accumulation caused by a temperature
us cri
gradient. In a nonmagnetic metal adjacent to the magnetic material, the spin currents
converge to the charge current through the inverse spin Hall effect 1. These mechanisms have been studied extensively and the power generation possible with such devices has increased 2–8. Since the voltage is perpendicular to the temperature gradient, power can be produced by using a uniform film, which could expand the range of applications for spin
an
Seebeck devices. However, the generated power is too small a practical use. The spin
Seebeck power is determined by the charge current generated in the nonmagnetic metal,
dM
which is calculated as below 9;
jc H
2e js ,
(1)
where jc is the charge current density, (ħ/2e) × js is the spin current density, σ is the unit vector for spin polarisation and H is the spin Hall angle of the nonmagnetic metal. In this
pte
paper, we focus on the spin Hall angle, which is an important parameter in determining the power generated by the spin Seebeck effect.
2.
Approaches
ce
The spin Hall angles H of typical nonmagnetic metals such as Pt 10–20, -Ta 13, 21 and -W 22, 23 have been studied extensively. Although the magnitudes of the spin Hall anglesof -Ta and -W are
generally larger than that of Pt, the spin Seebeck voltages of -Ta and -W are smaller than that of Pt 24,25.
To understand the disagreement between the spin Hall angle and the spin Seebeck voltage in a
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 2 of 15
pt
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
material, we attended to whether the magnetic material is a metal or an oxide. In this study, we took
2
rough averages to understand the difference between the magnetic metals and oxide, and the reported
us cri
spin Hall angle values were estimated from various sample structures and measurement systems. Figure 1 shows the average value of the spin Hall angle estimated simply from the values listed in Table I. For
each structure of magnetic metal and nonmagnetic metal (blue data), -Ta and -W have a larger H than that of Pt. In contrast, for each structure of magnetic oxide and nonmagnetic metal (red data), -Ta has a smaller H than that of Pt and the difference in H between -W and Pt is small. Even if we consider the effects of varying fabrication conditions and measurement methods on the H distribution, it is clear that
an
the spin Hall angle H depends on the nonmagnetic material and on the pairing of magnetic and nonmagnetic materials.
dM
Table I Reported spin Hall angle H for Pt, Ta and W in magnetic metal/nonmagnetic metal systems and magnetic oxide/nonmagnetic metal systems Structure
Nonmagnetic metal
pte
Pt
ce
Magnetic metal/ nonmagnetic metal
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
pt
Page 3 of 15
Ta W
3
H
Ref.
0.08
10
0.0013
11
0.013
12
0.021
13
0.068
14
0.006
15
0.08
16
0.022
17
0.012
18
0.027
19
0.02
20
0.0037
13
0.15
21
0.33
22
0.35
23
Structure
H
Nonmagnetic metal
0.04
Magnetic oxide/ nonmagnetic metal
Ta W
0.11
27
0.03
28
0.1
29
0.02
28
0.071
29
0.14
29
an
0.3
26
Magnetic metal/ nonmagnetic metal Magnetic oxide/nonmagnetic metal
dM
Average of reported spin Hall angle, |H|
0.5 0.4
Ref.
us cri
Pt
0.2 0.1
0
-Ta
-W
pte
Pt
Fig. 1 Average values of reported spin Hall angles H for Pt, Ta and W, calculated from the values in Table I.
ce
According to the Ellingham diagrams, Ta and W are easily oxidised as compared to Fe, which is the main element of magnetic oxides, e.g., Fe5Y3O12 (YIG) and Fe3O4, whereas Pt oxidises with more difficulty compared with Fe 30, 31. Therefore, we hypothesise that oxygen moves slightly from YIG to Ta and W at the interface. In that case, the spin mixing conductance at the interface between a magnetic
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 4 of 15
pt
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
oxide and a nonmagnetic metal should be reduced. In this study, to obtain both a large spin Hall angle H
4
as that of -W and high oxidation resistance as that of Pt, two approaches were utilised. First, we used a
us cri
nonmagnetic metal Ta50W50 alloy, which has a higher oxidation resistance than that of Ta or W alone 32.
Second, we inserted a thin layer of Ru between the YIG and nonmagnetic materials because Ru has high oxidation resistance. Although the sign of the spin Hall angle H of Ru is opposite to those of Ta and W, the magnitude of H for Ru is very small 33. The contribution of the Ru layer to the spin Hall angle can be restrained using a very thin sheet.
Experimental method
an
1.
Figure 2 shows a schematic of the sample structure and the spin Seebeck measurement system. The sample structures prepared for the first test are YIG/Pt (5 nm), YIG/Ta (5 nm), YIG/W (5 nm) and
dM
YIG/Ta50W50 (5 nm) and those for the second test are YIG/Ru (0.5 nm)/Ta (4.5 nm), YIG/Ru (0.5 nm)/W (4.5 nm) and YIG/Ru (0.5 nm)/Ta50W50 (4.5 nm), where YIG is the 1-mm-thick sintered bulk. The details of sample preparation are reported in a previous paper 34. The nonmagnetic layer shows resistivity of 77 cm, 1000 cm, 50 cm and 500 cm for Pt, Ta, W and Ta50W50, respectively. The resistivity of Ta, W and Ta50W50 are high enough to consider the materials as -phase tetragonal
pte
crystalline structures.
A temperature gradient was applied with a pair of Peltier modules, and we monitored the temperature difference T between the top and bottom of the sample. The temperature was monitored at the Peltier module surface within 1 mm from the sample surface; however, the monitored T could be slightly
ce
larger than the actual temperature difference between the top and bottom of sample. Once T was stabilised at 13 K or 18 K, a magnetic field was swept from −3 kOe to +3 kOe. The voltage generated was detected by 2 probes separated by 32 mm.
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
pt
Page 5 of 15
5
H
V
V
l=32mm
us cri
T
Nonmagnetic metal 5nm YIG 1mm
5mm
Fig. 2 Schematic of the sample structure and measurement system
Experimental results and discussion
an
2.
Before measuring the spin Seebeck voltage, we analysed the nonmagnetic metal Ta using X-ray photoelectron spectroscopy (XPS) to confirm oxidation at the interface. The sample structure for XPS was
dM
YIG (1 mm)/Ta (1 nm)/Al (2 nm). The thickness of the Ta layer was kept at 1 nm to emphasise the effect of the interface, and the top Al layer was sputtered to avoid atmospheric Ta oxidation. The XPS profiles for Al and Ta are shown in Fig. 3 (a) and (b), respectively. Majority of the Al layer was oxidised but some metallic Al remained, which indicates that the Al layer successfully blocked the atmospheric Ta oxidation.
ce
pte
The Ta–O peaks in Fig. 3 (b) indicate that Ta was oxidised at the interface with YIG.
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 6 of 15
pt
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
6
Intensity [a. u.]
Al 2p XPS of metal Al
65
pt
Al 2p XPS of AlOx
(a)
67
69
71
73 75 77 Binding Energy [eV]
79
81
83
85
17
19
an
Intensity [a. u.]
Ta 4f5/2of metal Ta (b) Ta 4f7/2 of metal Ta Ta 4f7/2 of TaOx
15
21 23 25 Binding Energy [eV]
27
29
31
dM
Fig. 3 XPS profiles of Al (a) and Ta (b) for the YIG (1 mm)/Ta (1 nm)/Al (2 nm) structure.
80 60 40 20 0 -20 -40 -60 -80
-0.3
-0.2
-0.1
0 H [T]
0.1
V [V]
Pt 5nm Ta 5nm W 5nm Ta50W50 5nm
pte
V [V]
(a)
0.2
0.3
(b) 80 60 40 20 0 -20 -40 -60 -80
Ru/Pt Ru/Ta Ru/W Ru/Ta50W50
-0.3
-0.2
-0.1
0 H [T]
0.1
0.2
ce
Fig. 4 Generated voltage V as a function of magnetic field H in a temperature
gradient T = 15 K for YIG 1 mm/Pt, Ta, W or Ta50W50 5 nm (a) and YIG 1 mm/Ru 0.5 nm/Pt, Ta, W or Ta50W50 4.5 nm (b), respectively.
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
us cri
Page 7 of 15
7
0.3
140
|S| [nV/K]
100
80 60 40 20 0 Ta Ta
W W
YIG
YIG
YIG
TaTaW 50W50
Ru/Ta Ta Ru YIG
Ru/W W
Ru YIG
Ru/TaW Ta50W50
5nm
0.5nm Ru YIG Bulk (1mm)
an
PtPt
us cri
120
YIG
Fig. 5 Magnitude of spin Seebeck coefficient |S| for YIG/nonmagnetic metals in 5-nm layers.
dM
Figure 4 shows the V–H curves for all samples when T was 15 K. The spin Seebeck voltage depends on the sign of the spin Hall angle. We found that the Ta50W50 alloy has a spin Hall angle with the same sign as Ta and W independently. Since the Ru layer is sufficiently thin, samples with Ru show the same before measuring the spin Seebeck voltage as those without Ru. We estimated the spin Seebeck coefficient |S| using the expression (tV)/(lT), where l is the probe distance of 32 mm and t is the YIG thickness of
pte
1 mm.
Figure 5 plots the absolute values of the spin |S| for all the studied samples. The YIG thickness that contributes to the spin Seebeck effect is about 100 nm. However, because our |S| was obtained by
ce
multiplying with the YIG total thickness of 1 mm, |S| is four orders of magnitude lower than its potential value. In Fig. 5, YIG/Ta has a smaller |S| than that of YIG/Pt, and YIG/W has mostly the same |S| as that of YIG/Pt. These results agree well with results reported in the literature 24,25. However, YIG/Ta50W50 did not exceed |S| as that of YIG/W. This indicates that the Ta50W50 alloy does not provide oxidation resistance
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 8 of 15
pt
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
at the YIG interface.
8
Ru is more resistive to oxidation than the Ta–W system, and its spin Hall angle is smaller than that of
us cri
other noble metals such as Pt. As a result, Ru insertion improves the absolute spin Seebeck coefficient |S| for nonmagnetic metals of Ta, W and Ta50W50, despite the fact that Ru has an spin Hall angle with an opposite sign. YIG/Ru/Ta50W50, in particular, achieved a 2.4 times higher |S| than the standard YIG/Pt. When comparing |S| between YIG/Ru/W and YIG/Ru/Ta50W50, we can neglect the difference of spin mixing conductance because both samples have the same interface, YIG/Ru. In that case, the spin
Seebceck coefficient |S| corresponds to the spin Hall angle. Therefore, the higher |S| of YIG/Ru/Ta50W50 relative to YIG/Ru/W indicates that Ta50W50 has a higher spin Hall angle than that of W. We found that
dM
an
Ta50W50 is the material with the highest spin Hall angle.
To estimate the effect of the spin Hall angles of Ru and Ta50W50 with opposite signs, we fabricated samples with YIG (1 mm)/Ru (t nm)/Ta50W50 (5 − t nm), where the Ru thickness t was varied from 0 to 5 nm and the Ta50W50 thickness was varied from 5 to 0 nm. The negative value of spin Seebeck coefficient −S in relation with the Ru thickness t is plotted in Fig. 6. −S was increased to a value more
pte
than its double by increasing the Ru thickness to 0.5 nm. However, once the Ru thickness is increased over 0.5 nm, −S starts decreasing and the sign changes at t = 4 nm, which indicates that the inverse spin Hall effect in Ru becomes dominant when the Ru layer is more than 4 nm thick. However |S| is small when the Ru thickness is over 4nm, the spin Seebeck voltage by the Ru layer is negligible compared to
ce
that by Ta50W50. In addition, there is possibility that the voltage is produced by the Nernst effect in the Ru layer. As |S| of the Ru 5nm is sufficiently small, it was found that the Nernst effect in Ru makes a
limited contribution.
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
pt
Page 9 of 15
Next, we estimated the ratio of improvement in |S| due to Ru insertion to gain insight into the influence
of Ru insertion on nonmagnetic materials; |S|YIG/Ru/Ta/|S|YIG/Ta = 3.6, |S|YIG/Ru/W/|S|YIG/W = 1.8 and
9
|S|YIG/Ru/Ta50W50/|S|YIG/Ta50W50 = 2.2. We found that structures with a large amount of Ta are sensitive to the
to the Ellingham diagram
us cri
improvement due to Ru insertion. Since Ta has a lower Gibbs standard energy than that of W according 30,31
, the recovery of spin mixing conductance is more pronounced in
nonmagnetic metals with a large amount of Ta.
As noted above, Ru insertion is intended to limit the oxidation of Ta, W and Ta50W50. The
improvement of |S| caused by Ru insertion suggests that the Ru layer indeed limits the oxidation of Ta, W and Ta50W50, which improves the spin mixing conductance at the interface with YIG. In contrast, the
an
spin Hall angle of W can be increased by intentional oxidation 35. We consider that optimum oxidation will improve the spin-orbit scattering and thereby increase the spin Hall angle; however, but uncontrolled oxidation at a local region such as the interface with YIG will intercept the spin current
100
Ru YIG
Ru
Ru
YIG
YIG
pte
- S [nV/K]
120
TaW
80 60
30 20 10 0 -10 -20 -30
-0.4
-0.2
5nm
YIG
30 20 10 0 -10 -20 -30 0.4
0
0.2
-0.4
H[T]
40
Ru
V[μ]V
160 YIG 140
TaW
TaW
V[μ]V
TaW
dM
injection and thereby decrease the spin mixing conductance.
-0.2
0
0.2
0.4
H[T]
20
0
-20
ce
0
1
2 3 Ru thickness [nm]
4
5
Fig. 6 Negative value of spin Seebeck coefficient−S for YIG (1 mm)/Ru (t nm)/Ta50W50 (5 − t nm).
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 10 of 15
pt
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
10
us cri
3.
Summary
We showed that YIG/Ru/Ta50W50 has a 2.4 times higher spin Seebeck coefficient than conventional YIG/Pt. By comparing the spin Seebeck coefficients for YIG/Ru/W and YIG/Ru/Ta50W50, we found that the spin Hall angle of Ta50W50 is larger than that of W. Since inserting Ru into the interface between YIG and nonmagnetic metal successfully improved the spin mixing conductance at the interface, Ru proves to
an
be a suitable insertion material of improving the spin mixing conductance for YIG/Ta–W systems. These systems have a high spin Hall angle but are easily oxidised. To design devices that require specific spin Hall angle and spin mixing conductance, materials for the bulk and interface should be selected separately
Acknowledgements
dM
to improve the spin Seebeck coefficient.
We would like to thank Prof. Fujigaya and the Nanotechnology Platform Programme (Molecule and Material Synthesis) of MEXT, Japan, for XPS analysis. This work was supported by the PRESTO-JST
pte
(JPMJPR15R8), the Tateisi Science and Technology Foundation, the Spin Research Network of Japan and the JSPS KAKENHI (JP16K13617).
References 1
K. Uchida, S. Takahashi, K. Harii, J. Ieda, W. Koshibae, K. Ando, S. Maekawa & E. Saitoh, Nature
ce
455, 778 (2008).
2
K. Uchida, J. Xiao, H. Adachi, J. Ohe, S. Takahashi, J. Ieda, T. Ota, Y. Kajiwara,H. Umezawa, H. Kawai, G. E.W. Bauer, S. Maekawa and E. Saitoh, Nature materials. 9, 894 (2010).
3
K. Uchida, H. Adachi, T. Ota, H. Nakayama, S. Maekawa and E. Saitoh, Appl. Phys. Lett. 97, 172505
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
pt
Page 11 of 15
(2010).
11
4
S.Y. Huang, W. G. Wang, S. F. Lee, J. Kwo, and C. L. Chien, Phys. Rev. Lett. 107, 216604 (2011).
5
N. Roschewsky, M. Schreier, A. Kamra, F. Schade,
us cri
K. Ganzhorn, S. Meyer, H. Huebl, S. Gepr€ags,
R. Gross, and S. T. B. Goennenwein, Appl. Phys. Lett. 104, 202410 (2014). 6
A. Kirihara, K. Uchida, Y. Kajiwara, M. Ishida, Y. Nakamura, T. Manako, E. Saitoh, and S. Yorozu, Nat. Mater. 11, 686 (2012).
7
R. Ramos, T. Kikkawa, A. Anadón, I. Lucas, K. Uchida, P. A. Algarabel, L. Morellón, M. H. Aguirre, E. Saitoh, and M. R. Ibarra, AIP ADVANCES 7, 055915 (2017).
K. Uchida, H. Adachi, T. Kikkawa, A. Kirihara, M. Ishida, S. Yorozu, S. Maekawa, E. Saitoh ,
an
8
Proceedings of the IEEE 104, 1946 (2016).
Y. Tserkovnyak, A. Brataas, and G. Bauer, Phys. Rev. B 66, 224403 (2002).
10
K. Ando, S. Takahashi, K. Harii, K. Sasage, J. Ieda, S. Maekawa, and E.Saitoh, Phys. Rev. Lett. 101, 036601 (2008).
11
dM
9
O. Mosendz, J. E. Pearson, F. Y. Fradin, G. E. W. Bauer, S. D. Bader, and A. Hoffmann, Phys. Rev. Lett. 104, 046601 (2010).
O. Mosendz V. Vlaminck, J. E. Pearson, F. Y. Fradin, G. E. W. Bauer, S. D. Bader, and A.
pte
12
Hoffmann, Phys. Rev. B 82, 214403 (2010). 13
M. Morota, Y. Niimi, K. Ohnishi, D. H. Wei, T. Tanaka, H. Kontani, T. Kimura, and Y. Otani, Phys. Rev. B 83, 174405 (2011).
L. Q. Liu, T. Moriyama, D. C. Ralph, and R. A. Buhrman, Phys. Rev. Lett. 106, 036601 (2011).
ce
14
15
K. Ando, S. Takahashi, J. Ieda, Y. Kajiwara, H. Nakayama, T. Yoshino, K. Harii, Y. Fujikawa, M. Matsuo, S.Maekawa, and E. Saitoh, J. Appl. Phys., 109 103913 (2011).
16
A. Azevedo, L. H. Vilela-Leão, R. L. Rodríguez-Suárez, A. F. L. Santos, and S. M. Rezende, Phys.
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 12 of 15
pt
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
Rev. B, 83, 144402 (2011).
12
17
K. Kondou, H. Sukegawa, S. Mitani, K. Tsukagoshi, and S. Kasai, Appl. Phys. Exp., 5, 073002
18
us cri
(2012).
Z. Feng, J. Hu, L. Sun, B. You, D.Wu, J. Du, W. Zhang, A. Hu, Y. Yang, D. M. Tang, B. S. Zhang, and H. F. Ding, Phys. Rev. B 85, 214423 (2012).
19
V. Vlaminck, J. E. Pearson, S. D. Bader, and A. Hoffmann, Phys. Rev. B. 88 064414 (2013).
20
H. Y. Hung, G. Y. Luo, Y. C. Chiu, P. Chang, W. C. Lee, J. G. Lin, S. F. Lee, M. Hong, and J. Kwo, J.Appl. Phys., 113, 17C507 (2013).
L. Q. Liu, C. -F. Pai, Y. Li, H. W. Tseng, D. C. Ralph, and R. A. Buhrman, Science 336, 555 (2012).
22
C. -F. Pai, L. Liu, Y. Li, H. W. Tseng, D. C. Ralph, and R. A. Buhrman, Appl. Phys. Lett.101,
an
21
122404 (2012)
Q. Hao and G. Siao, Phys. Rev. Appl. 3, 034009 (2015).
24
M. Ishida, A. Kirihara, H. Someya, K. Uchida, S. Kohmoto, E. Saitoh, T. Murakami:
dM
23
arXiv:1307.3320 [cond-mat.mtrl-sci] (Submitted on 12 Jul 2013) 25
N. Vlietstra, J. Shan, and B. J. van Wees, M. Isasa, F. Casanova, J. Ben Youssef, Phys. Rev. B 90, 174436 (2014).
26
H. Nakayama, M. Althammer, Y.-T. Chen, K. Uchida, Y. Kajiwara, D. Kikuchi, T. Ohtani, S.
pte
Geprags, M. Opel, S. Takahashi, R. Gross, G. E.W. Bauer, S. T. B. Goennenwein, and E. Saitoh, Phys. Rev. Lett. 110, 206601 (2013). 27
M. Althammer, S. Meyer, H. Nakayama, M. Schreier, S. Altmannshofer, M. Weiler, H. Huebl, S. Gepr¨ags, M. Opel, R. Gross, D. Meier, C. Klewe, T. Kuschel, J.-M. Schmalhorst, G. Reiss, L.
ce
Shen, A. Gupta, Y.-T. Chen, G. E. W. Bauer, E. Saitoh, and Sebastian T. B. Goennenwein, Phys. Rev. B 87, 224401 (2013).
28
C. Hahn, G. de Loubens, O. Klein, M. Viret, V. V. Naletov, and J. Ben Youssef, Phys. Rev. B 87, 174417 (2013).
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
pt
Page 13 of 15
13
29
H. L. Wang, C. H. Du, Y. Pu, R. Adur, P. C. Hammel, and F. Y. Yang, Phys. Rev. Lett. 112, 197201
us cri
(2014). 30
H. J. T. Ellingham, J. Soc. Chem. Ind. 63, 125 (1944)
31
Peter Atkins, de Paula, Julio (2006), Physical Chemistry: Thermodynamics And Kinetics (8th ed.), W.H. Freeman, p. 215, ISBN 0716785676. This reference plots the diagram upside-down, with ΔG° decreasing upwards.
32
R. Yoda and T. Itagaki, J. Japan Inst.Met.Mater. 36, 1121 (1972) (in Japanese).
33
T. Tanaka, H. Kontani, M. Naito, D. S. Hirashima, K. Yamada, and J. Inoue, Phys. Rev. B 77,
an
165117 (2008).
H. Yuasa, K. Tamae, and N. Onizuka, AIP Advances 7, 055928 (2017).
35
K.-U. Demasius., T. Phung, W. Zhang, B. P. Hughes, S.-H. Yang, A. Kellock, W. Han, A. Pushp and
dM
34
S. S. P. Parkin, Nat. Comm. 7 10644 (2016).
Figure Captions
Table I.
pte
Fig. 1 Average values of reported spin Hall angles H for Pt, Ta and W, calculated from the values in
ce
Fig. 2 Schematic of the sample structure and measurement system.
Fig. 3 XPS profiles of Al (a) and Ta (b) for the YIG (1 mm)/Ta (1 nm)/Al (2 nm) structure. Fig. 4 Generated voltage V as a function of magnetic field H in a temperature gradient T = 15 K for YIG 1 mm/Pt, Ta, W or Ta50W50 5 nm (a) and YIG 1 mm/Ru 0.5 nm/Pt, Ta, W or Ta50W50 4.5 nm (b),
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
Page 14 of 15
pt
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
respectively.
14
Fig. 5 Magnitude of spin Seebeck coefficient |S| for YIG/nonmagnetic metals in 5-nm layers.
us cri
Fig. 6 Negative value of spin Seebeck coefficient−S for YIG (1 mm)/Ru (t nm)/Ta50W50 (5 − t
ce
pte
dM
an
nm).
Ac
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60
AUTHOR SUBMITTED MANUSCRIPT - JPhysD-115682.R1
pt
Page 15 of 15
15